Heidelberg Materials - EPDs - Offers a comprehensive range of building materials such as cement, aggregates, ready-mixed concrete, and asphalt, known for quality and innovation.

Heidelberg Materials is a leading global manufacturer of building materials, including cement, aggregates, ready-mixed concrete, and asphalt, serving the construction industry worldwide.

Offers a comprehensive range of building materials such as cement, aggregates, ready-mixed concrete, and asphalt, known for quality and innovation.

Website: https://www.heidelbergmaterials.com

Email: Annika.Fuchs@heidelbergmaterials.com

Phone: +49 6221 48113227

Address:

Heidelberg Materials AG, Berliner Strasse 6, 69120 Heidelberg, Germany

EPDs (11927)•Sorted by date

Ready-mix concrete, 20 MPa at 28 days; Cement type: Manufacturer specific, Mix 20D04GM1, Lehigh Hanson Materials, Kelowna plant

Lehigh Hanson Materials, Kelowna plant

231 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C4001AP, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

248 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix EZ30D0XB2C60, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

224 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E0YB3D08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

174 kg CO2e/m³

Ready-mix concrete, 60 MPa at 56 days; Cement type: Manufacturer specific, Mix GC60D0XB2D13, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

290 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix FM30E3XB2C11, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

230 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix GC35E5XB2C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

258 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix GC45E0XB1C11, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

262 kg CO2e/m³

Ready-mix concrete, 40 MPa at 28 days; Cement type: Manufacturer specific, Mix TC40E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

235 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E0XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

208 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix GC25E3YB7D08, Lehigh Hanson Materials, Victoria plant

Lehigh Hanson Materials, Victoria plant

147 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix 30ICF829, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

156 kg CO2e/m³

Ready-mix concrete, 35 MPa at 56 days; Cement type: Manufacturer specific, Mix HT35A0XB3D70, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

249 kg CO2e/m³

Ready-mix concrete, 4500 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J15501B, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

214 kg CO2e/m³

Ready-mix concrete, 50 MPa at 56 days; Cement type: Manufacturer specific, Mix TA50D0YB7D11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

285 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C24010, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

288 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix GC35E5XB2C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

258 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C4001AP, Corliss Resources Inc., Enumclaw plant

Corliss Resources Inc., Enumclaw plant

242 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix RG25E3YB5D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

153 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix FM30E3XB2C11, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

230 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E0XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

195 kg CO2e/m³

Ready-mix concrete, 40 MPa at 28 days; Cement type: Manufacturer specific, Mix TC40E0XB1C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

278 kg CO2e/m³

Ready-mix concrete, 5000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KCIP5000L, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

270 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KLP3000L, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

170 kg CO2e/m³

Ready-mix concrete, 35 MPa at 56 days; Cement type: Manufacturer specific, Mix HT35A0YB6D70, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

206 kg CO2e/m³

Ready-mix concrete, 40 MPa at 28 days; Cement type: Manufacturer specific, Mix GS40D5XB7C06, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

255 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix GC35E0XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

275 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

176 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix RG25E3XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

193 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix P23010, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

221 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix TD35E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

208 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix TD35E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

208 kg CO2e/m³

Ready-mix concrete, 45 MPa at 56 days; Cement type: Manufacturer specific, Mix GC45E0YB3D11, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

213 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

211 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix LH30E0YB6D08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

173 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix EZ30D0XB2C60, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

224 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix LH25E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

153 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix GC35E0XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

251 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix P2401A, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

274 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix CR3000, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

196 kg CO2e/m³

Ready-mix concrete, 4500 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J15501AB, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

229 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E0XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

193 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J16000, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

265 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E3YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

168 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix TD35E0XB1C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

247 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GL30D0XB1C13, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

220 kg CO2e/m³

Ready-mix concrete, 5000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J16500, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

286 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix GC45E0XB2C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

246 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C1301A, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

219 kg CO2e/m³

Ready-mix concrete, 2500 psi; Curing time 1 days; Cement type: Manufacturer specific, Mix J3800A1D, Corliss Resources Inc., Enumclaw plant

Corliss Resources Inc., Enumclaw plant

348 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix TD30E0XB2C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

222 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix LH25E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

153 kg CO2e/m³

Ready-mix concrete, 6000 psi; Curing time 56 days; Cement type: Manufacturer specific, Mix KCIP6000L1, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

286 kg CO2e/m³

Ready-mix concrete, 40 MPa at 28 days; Cement type: Manufacturer specific, Mix TC40E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

235 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix RG25E3XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

193 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E0XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

195 kg CO2e/m³

Ready-mix concrete, 32 MPa at 56 days; Cement type: Manufacturer specific, Mix RL32D5YB5D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

194 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GC30D0XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

227 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C4000AD, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

273 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KWLSC4000L, Corliss Resources Inc., Enumclaw plant

Corliss Resources Inc., Enumclaw plant

258 kg CO2e/m³

Ready-mix concrete, 32 MPa at 28 days; Cement type: Manufacturer specific, Mix GC32K3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

251 kg CO2e/m³

Ready-mix concrete, 35 MPa at 56 days; Cement type: Manufacturer specific, Mix GC35E5YB5D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

208 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J155002, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

247 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C1601A, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

250 kg CO2e/m³

Ready-mix concrete, 5000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KCIP5000L, Corliss Resources Inc., Federal Way plant

Corliss Resources Inc., Federal Way plant

266 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix 35D07PL1, Lehigh Hanson Materials, Kelowna plant

Lehigh Hanson Materials, Kelowna plant

283 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E0XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

195 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KWLSC4000L, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

267 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix TB45E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

269 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix J24010, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

236 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GL30D0XB1C13, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

232 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

211 kg CO2e/m³

Ready-mix concrete, 25 MPa at 28 days; Cement type: Manufacturer specific, Mix GC25E3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

211 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix S15000, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

217 kg CO2e/m³

Ready-mix concrete, 40 MPa at 28 days; Cement type: Manufacturer specific, Mix TC40E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

235 kg CO2e/m³

Ready-mix concrete, 50 MPa at 56 days; Cement type: Manufacturer specific, Mix TA50D0YB7D11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

285 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

176 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E3YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

168 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix LH25E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

153 kg CO2e/m³

Ready-mix concrete, 32 MPa at 28 days; Cement type: Manufacturer specific, Mix GC32D0XB1C08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

228 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix TD30E0XB2C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

222 kg CO2e/m³

Ready-mix concrete, 25 MPa at 56 days; Cement type: Manufacturer specific, Mix LH25E3YB3D08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

151 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix LH30E0YB6D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

171 kg CO2e/m³

Ready-mix concrete, 60 MPa at 56 days; Cement type: Manufacturer specific, Mix GC60D0XB2D13, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

290 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix GC45E0XB1C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

259 kg CO2e/m³

Ready-mix concrete, 3000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix L1301A30, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

185 kg CO2e/m³

Ready-mix concrete, 20 MPa at 56 days; Cement type: Manufacturer specific, Mix GC20E0YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

151 kg CO2e/m³

Ready-mix concrete, 50 MPa at 56 days; Cement type: Manufacturer specific, Mix TA50D0YB7D11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

285 kg CO2e/m³

Ready-mix concrete, 35 MPa at 56 days; Cement type: Manufacturer specific, Mix GC35E3YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

207 kg CO2e/m³

Ready-mix concrete, 35 MPa at 28 days; Cement type: Manufacturer specific, Mix 35D07PL1, Lehigh Hanson Materials, Kelowna plant

Lehigh Hanson Materials, Kelowna plant

283 kg CO2e/m³

Ready-mix concrete, 5000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KDS5000L, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

250 kg CO2e/m³

Ready-mix concrete, 32 MPa at 28 days; Cement type: Manufacturer specific, Mix GC32E5XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

255 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix GC45E5XB2C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

297 kg CO2e/m³

Ready-mix concrete, 30 MPa at 56 days; Cement type: Manufacturer specific, Mix GC30E3YB3D08, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

168 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GC30E3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

242 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GC30E3XB1C08, Lehigh Hanson Materials, Langley plant

Lehigh Hanson Materials, Langley plant

242 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix KWLSC4000L, Corliss Resources Inc., Sumner plant

Corliss Resources Inc., Sumner plant

246 kg CO2e/m³

Ready-mix concrete, 45 MPa at 28 days; Cement type: Manufacturer specific, Mix TB45E0YB7C11, Lehigh Hanson Materials, Mitchell Island plant

Lehigh Hanson Materials, Mitchell Island plant

269 kg CO2e/m³

Ready-mix concrete, 4000 psi; Curing time 28 days; Cement type: Manufacturer specific, Mix C24010, Corliss Resources Inc., Puyallup plant

Corliss Resources Inc., Puyallup plant

292 kg CO2e/m³

Ready-mix concrete, 30 MPa at 28 days; Cement type: Manufacturer specific, Mix GC30E0XB1C08, Lehigh Hanson Materials, North Vancouver Plant plant

Lehigh Hanson Materials, North Vancouver Plant plant

231 kg CO2e/m³

Previous 1 2 3...113...118 119 120 Next